Top Quality Alumina Ceramic Foam Filter (Molten metal filter)

• Customization: Available
• Application: Refractory, Alumina Alloy Foundry
• Feature: Long Time Materials
• Model NO.: CFA
• Ppi: 10-60ppi
• Thickness: 12-25mm
• Type: Refractory Material
• Refractoriness (℃): 1200 Celsius Degree
• Material: Alumina
• Transport Package: Export Package: Wooden Box+Pallet
• Specification: Diameter=30~500mm H=5~20mm
• Trademark: DXY
• Origin: China
• HS Code: 842199900
• Production Capacity: 100, 000pieces/Month

Product Description

Alumina ceramic foam filter is mainly for filtration of aluminum and aluminum alloys in foundries and cast houses. With their excellent resistance to attack and corrosion from molten aluminum, they can effectively remove inclusions, reduce trapped gas and provide laminar flow, and then the filtered metal is significantly clearner. Clearner metal results in higher-quality castings, less scrap, and fewer inclusion defects, all of which contribute to bottom-line profit

Alumina ceramic foam filter can be made by specific procedures and have peculiar bone-frame holes just like the shape of foam (Called three-dimensional connected channel) and myriad eyelets which only been found in big times microscope. The three-dimensional structure can improve the cast quality in large scale by changing the molten metal from turbulence flow to lamellar flow, removing the gas and smoothing the casting. Ceramic foam filter is not only applied for molten metal filtering in high temperature, but gas treatment in high temperature, carrier of catalyzer, solid heat exchange and advanced filling for chemical industry compare to similar ones.

Features:
*Stable chemical composition
*Excellent strength
*Resistant to high temperature
*Calm down of the turbulent flow of metal nicely
*Big m2/m3
*Superior dimensional tolerances: +0/-2.5

Thickness mm	Aperture PPi	Volume intensity g/cm3	Tortuous intensity in  normal temperature N/cm2	Pressure resistence intensity in normal temperature N/cm2	Pressure resistence intensity in high temperature N/cm2	Refractory temperature	Air discharging capability cm3/g	Porosity %
15-100	10-45	0.35-0.45	≥38	≥80	≥45	≥1800	≤5	≥85

 

Specification mm	Area M2	Maximum metal volume of pouring (kg/min)	Optimum volume of pouring (kg/min)	Typical capacity of filtering (T)
178X178X50	0.0213	57.00	25-45	4.2
229X229X50	0.0387	118.00	35-102	6.9
305X305X50	0.0745	198.00	90-165	13.8
381X381X50	0.122	325.80	130-265	23.2
432X432X50	0.160	427.20	210-350	34.5
508X508X50	0.227	606.60	280-465	43.7
585X585X50	0.341	772.20	370-540	57.3