Al2O3/Sic/Zirconia/MGO Ceramic Foam Filter (Material: Silicon carbide, Alumina, Zirconia, Magnesia)

• Customization: Available
• Application: Refractory
• Type: Refractory Material
• Model NO.: CFF
• Porosity(%): 80-90
• Ppi: 10-60
• Refractoriness (ºC): 1580< Refractoriness< 1770
• Feature: Long Time Materials
• Shape: Square, Rectangle, etc
• Material: Alumina, Sic, Zirconia
• Transport Package: Wooden Box/Carton Box with Pallet
• Specification: 50*50*12mm, 149.63/141.79*200*15, 250*200*15mm, et
• Trademark: DXY
• Origin: China
• Production Capacity: 100, 000pieces/Month

Product Description

Ceramic foam filter is just developed as a new type of molten metal filters to decrease casting flaw in recent years. It is made from high quality ceramic materials, whose main components are Al2O3, Sic, ZrO2, MgO etc. Ceramic Foam Filter has the characters of light weight, high mechanical strength, large specific surface areas, high porosity, excellent thermal shock resistance, chemical corrosion resistance and high temperature stability in molten metal. With the distributing pores net structure, they are able to increase the surface areas, and absorb the sinter, the liquid metal becomes more pure, waster quality problems such as sand pore and air pore are much less and the cast quality becomes much better.

We can supply ceramic foam filters are as follows:
*Silicon Carbide Ceramic Foam Filter is applied to purge and filter solution of ductile iron casting, grey iron and other iron casting.
*Zirconia Ceramic Foam Filter is applied to purge and filter solution of steel high temperature metal such as steel alloy stainless steel etc.
*Magnesia Ceramic Foam Filter is applied to purge and filter solution of magnesium and magnesium alloy.
*Alumina Ceramic Foam Filter is applied to purge and filter solution of aluminium and aluminium alloys.

Type	Alumina CFF	Silicon carbide CFF	Zirconia CFF	Magnesia CFF
Material	Al2O3	Sic	ZrO2	MgO
Applied temperature	≤1200 Degree C	≤1500 Degree C	≤1700 Degree C	≤1100 Degree C
Color	White	Grey black	Yellow	Yellow
Bulk Density	0.35~0.55g/cm3	0.45~0.65g/cm3	1~1.5g/cm3	0.5~0.7g/cm3
Bore Density	10~60PPI	10~60PPI	10~60PPI	10-60ppi
Porosity	80~90%	80~90%	80~90%	80-90%
Bending Strength	0.6Mpa	0.8Mpa	0.8-1.0Mpa	0.6Mpa
Compression Strength	≥0.8Mpa	≥1.0Mpa	≥1.5Mpa	≥0.8Mpa
Thermal Shock Resistance (1100 Degree C ~ Room Temperature)	Not break after 6 times thermal shock testing
Application	Molten Aluminum and Alloy	Molten Iron and Alloy	Molten Stainless Steel, Alloy and other metal in precision molding	Molten magnesium and its alloys