Sic/Alumina/Zirconia Porous Ceramic Foam Filters for Iron Casting

• Customization: Available
• Material: Zirconia Oxide
• Refractoriness (℃): Refractoriness> 2000
• Model NO.: FCF
• Usage: Steel Iron Casting
• Ppi: 10-60ppi
• Thickness: 12-25mm
• Feature: Long Time Materials
• Type: Refractory Material
• Transport Package: Export Package: Wooden Box+Pallet
• Trademark: DXY
• Origin: China
• HS Code: 842199900
• Production Capacity: 100, 000pieces/Month

Product Description

Ceramic foam filter is just developed as a new type of molten metal filters to decrease casting 
flaw in recent years. It is made from high quality ceramic materials, whose main components 
are Al2O3, SiC, ZrO2, MgO etc. Ceramic Foam Filter has the characters of light weight, high 
mechanical strength, large specific surface areas, high porosity, excellent thermal shock resistance, 
chemical corrosion resistance and high temperature stability in molten metal. With the distributing 
pores net structure, they are able to increase the surface areas, and absorb the sinter, the liquid metal 
becomes more pure, waster quality problems such as sand pore and air pore are much less and 
the cast quality becomes much better.
 
We can supply ceramic foam filters are as follows:
1. Silicon Carbide Ceramic Foam Filter is applied to purge and filter solution of ductile iron 
casting, grey iron and other iron casting.
2. Zirconia Ceramic Foam Filter is applied to purge and filter solution of steel high temperature 
metal such as steel alloy stainless steel etc.
3. Magnesia Ceramic Foam Filter is applied to purge and filter solution of magnesium and 
magnesium alloy.
4. Alumina Ceramic Foam Filter is applied to purge and filter solution of aluminium and 
aluminium alloys.
 
Specifications Ceramic Foam Filter for foundry iron/steel/alumina casting 
1.Material: Al2O3, SiC, ZrO2, MgO 
2.Bore density: 10-60 PPI

Type	Alumina CFF	Silicon carbide CFF	Zirconia CFF	Magnesia CFF
Material	Al2O3	Sic	ZrO2	MgO
Applied temperature	≤1200 º C	≤1500 º C	≤1700 º C	≤1100 º C
Color	White	Grey black	Yellow	Yellow
Bulk Density	0.35~0.55g/cm3	0.45~0.65g/cm3	1~1.5g/cm3	0.5~0.7g/cm3
Bore Density	10~60PPI	10~60PPI	10~60PPI	10-60ppi
Porosity	80~90%	80~90%	80~90%	80-90%
Bending Strength	0.6Mpa	0.8Mpa	0.8-1.0Mpa	0.6Mpa
Compression Strength	≥0.8Mpa	≥1.0Mpa	≥1.5Mpa	≥0.8Mpa
Thermal Shock Resistance	Not break after 6 times thermal shock testing
(1100 º C ~ Room Temperature)
Application	Molten Aluminum and Alloy	Molten Iron and Alloy	Molten Stainless Steel, Alloy and other metal in precision molding	Molten magnesium and its alloys